Welding Holders

Welding Electrodes For Stainless Steels:

Electrodes Number International Equals Foreign Equals Ob o5 Main Welding Chemical Coposition
USA : AWS JAP : JIS
      MPa % C Mn Si Cr Ni Mo Nb
G202 E410-16 E410-16   450 20 0.12 1 0.9 11.0 - 13.5 0.7 0.75 Cu ≤ 0.75
G207 E410-15 E410-15   450 20 0.12 1 0.9 11.0 - 13.5 0.7 0.75 Cu ≤ 0.75
A002 E308L-16 E308L-16   520 35 0.04 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 Cu ≤ 0.75
A002Nb     D347L-16 510 30 0.04 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 - 8xC - 1.0
A002Mo E308MoL-16     520 35 0.04 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 12.0 2.0 - 3.0 Cu ≤ 0.75
A022 E316L-16 E316L-16   490 30 0.04 0.5 - 2.5 0.9 17.0 - 20.0 11.0 - 14.0 2.0 - 3.0 Cu ≤ 0.75
A032 E317MoCUL-16     540 25 0.04 0.5 - 2.5 0.9 18.0 - 21.0 12.0 - 14.0 2.0 - 3.5 Cu ≤ 2.0
A052       490 25 0.04 2 1 17.0 - 20.0 22.0 - 27.0 4.0 - 5.5 Cu ≤ 2.0
A062 E309L-16 E309L-16   520 25 0.04 0.5 - 2.5 0.9 22.0 - 25.0 12.0 - 14.0 0.75 Cu ≤ 0.75
A101 E308-16 E308L-16   550 35 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 Cu ≤ 0.75
A102 E308-16 E308L-16   550 35 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 Cu ≤ 0.75
A102T E308-16 E308L-16   550 35 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 Cu ≤ 0.75
A107 E308-15 E308L-15   550 35 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 Cu ≤ 0.75
A112       540 25 0.12 2.5 1.5 17.0 - 20.0 7.0 - 11.0 - 8 x C-1.0 Cu ≤ 0.75
A132 E347-16 E347-16   520 25 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 8 x C-1.0 Cu ≤ 0.75
A132A E347-17 E347-17   520 25 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 8 x C-1.0 Cu ≤ 0.75
A137 E347-15 E347-15   520 25 0.08 0.5 - 2.5 0.9 18.0 - 21.0 9.0 - 11.0 0.75 8 x C-1.0 Cu ≤ 0.75
A201 E316-16 E316-16   520 30 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 - 20.0 2.0 - 3.0 Cu ≤ 0.75
A202 E316-16 E316-16   520 30 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 - 20.0 2.0 - 3.0 Cu ≤ 0.75
A207 E316-15 E316-15   550 30 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 - 20.0 2.0 - 3.0 Cu ≤ 0.75
A212 E318-16 E318-16   540 25 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 - 20.0 2.0 - 3.0 6 x C-1.0 Cu ≤ 0.75
A222 E317MoCu-16     540 25 0.08 0.5 - 2.5 0.9 18.0 - 21.0 18.0 - 21.0 2.0 - 2.5 Cu ≤ 2.0
A232 E318V-16     540 25 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 20.0 2.0 - 2.5 V0.30 - 0.71 Cm ≤ 0.5
A237 E318V-15     550 25 0.08 0.5 - 2.5 0.9 17.0 - 20.0 17.0 20.0 2.0 - 2.5 V0.30 - 0.71 Cm ≤ 0.5
A242 E317-16 E317-16   550 25 0.08 0.5 - 2.5 0.9 18.0 - 21.0 18.0 - 21.0 304 - 4.0 Cu ≤ 0.75
A301 E309-16 E309-16   550 25 0.15 0.5 - 2.5 0.9 22.0 - 25.0 22.0 - 25.0 0.75 Cu ≤ 0.75
A302 E309-16 E309-16   550 25 0.15 0.5 - 2.5 0.9 22.0 - 25.0 22.0 - 25.0 0.75 Cu ≤ 0.75
A307 E309-15 E309-15   550 25 0.15 0.5 - 2.5 0.9 22.0 - 25.0 22.0 - 25.0 0.75 Cu ≤ 0.75
A312 E309Mo-16 E309Mo-16   550 25 0.12 0.5 - 2.5 0.9 22.0 - 25.0 22.0 - 25.0 2.0 - 3.0 Cu ≤ 0.75
A317 E309Mo-15 E309Mo-15   550 25 0.12 0.5 - 2.5 0.9 22.0 - 25.0 22.0 - 25.0 2.0 - 3.0 Cu ≤ 0.75
A402 E310-16 E310-16   550 25 0.08 - 0.20 1.5 - 2.5 0.75 25.0 - 28.0 22.0 - 28.0 0.75 Cu ≤ 0.75
A407 E310-15 E310-15   550 25 0.08 - 0.20 1.5 - 2.5 0.75 25.0 - 28.0 22.0 - 28.0 0.75 Cu ≤ 0.75
A412 E310Mo-16 E310Mo-16   550 25 0.12 1.5 - 2.5 0.75 25.0 - 28.0 22.0 - 28.0 2.0 - 3.0 Cu ≤ 0.75

Note: The properties listed in the table are the min. Value and the chemical composition values are max.

 

Welding Electrodes For Carbon Steels:

Electrodes Number International Equals Foreign Equals Tensile Strength Yielding Point Elogination Impact Value Content of Diffusible Hydrogen X-ray Inspection
USA : AWS JAP : JIS
GB / T5117 - 1995 E6013 D4313 MPa MPa % °CJ ml/100g Grade
J421 E4313 E6013 D4313 420 330 17 - - 2
J421Fe E4313 E6024 D4324 420 330 17 - - 2
J421Fe13 E4324 E6024   420 330 17 - - 2
J421Fe16 E4324   D4303 420 330 22 0.27 - 2
J422 E4303   D4303 420 330 22 0.27 - 2
J422Fe E4303   D4324 420 330 22 0.27 - 2
J422Fe13 E4323     420 330 22 0.27 - 2
J422Fe16 E4323     420 330 22 0.27 - 2
J422CrCU E4303     420 330 22 0.27 - 2
J422CuCrNi E4301   D4301 420 330 22 0.27 - 2
J423 E4301     420 330 22 0.27 - 2
J424 E4320 E6020   420 400 17 - - 2
J425 E4311 E6011   420 400 17 -30,27 - 2
J426 E4316 E6016   420 400 20 -30,27 ≤8 1
J426Fe13 E4328 E6028   420 400 20 -30,27 ≤8 1
J427 E4315 E6015   420 400 22 -30,27 ≤8 1
J427Ni E4315 E7015   420 400 20 -40,27 ≤8 1
J501Fe E5014 E7014   490 400 17 0,27 - 2
J501Fe15 E5024 E7024   490 400 17 0,27 - 2
J502 E5003   D5003 490 400 20 0,27 - 2
J502Fe E5003   D5003 490 400 20 0,27 - 2
J502Fe16 E5023 E7023   490 400 22 0,27 - 2
J503 E5001 E7001   490 400 20 0,27 - 2
J505 E5011 E7011   490 400 20 -30,27 - 2
J506 E5016 E7016   490 400 22 -30,27 ≤8 1
J506Fe E5018     490 400 22 -30,27 ≤8 1
J506X E5016     490 400 22 -30,27 ≤8 1
J506Fe-1 E5018-1     490 400 23 -46,27 ≤8 1
J506Fe16 E5028     490 400 22 -20,27 ≤8 2
J507 E5015     490 400 22 -30,27 ≤8 1
J507XG E5015     490 400 22 -30,27 ≤8 1
J507Fe E5018     490 400 22 -30,27 ≤8 1
J507Fe16 E5028     490 400 22 -20,27 ≤8 2

Note: The properties listed in the table are the min. Value and the chemical composition values are max.